A study on stress corrosion cracking and hydrogen embrittlement of Jethete M152 martensitic stainless steel | |
Shen, Sicong; Song, Xiaolong; Li, Qizhen; Li, Xinfeng; Zhu, Ruihua; Yang, Gongxian | |
刊名 | Materials Science and Engineering A |
2019 | |
卷号 | 740页码:243-251 |
关键词 | Constant loads Corrosive environment Fractographic analysis Fracture morphology Hydrogen charging Inclusion sizes Lath martensite Slow strain rates |
ISSN号 | 0921-5093 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2826477 |
专题 | 西安交通大学 |
推荐引用方式 GB/T 7714 | Shen, Sicong,Song, Xiaolong,Li, Qizhen,et al. A study on stress corrosion cracking and hydrogen embrittlement of Jethete M152 martensitic stainless steel[J]. Materials Science and Engineering A,2019,740:243-251. |
APA | Shen, Sicong,Song, Xiaolong,Li, Qizhen,Li, Xinfeng,Zhu, Ruihua,&Yang, Gongxian.(2019).A study on stress corrosion cracking and hydrogen embrittlement of Jethete M152 martensitic stainless steel.Materials Science and Engineering A,740,243-251. |
MLA | Shen, Sicong,et al."A study on stress corrosion cracking and hydrogen embrittlement of Jethete M152 martensitic stainless steel".Materials Science and Engineering A 740(2019):243-251. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论