The Enhanced Electrochemical Performance of Nanocrystalline Li[Li0.26Ni0.11Mn0.63]O-2 Synthesized by the Molten-Salt Method for Li-ion batteries | |
Wang ZhenYao ; Li Biao ; Ma Jin ; Xia DingGuo | |
刊名 | 电化学学报 |
2014 | |
关键词 | Lithium rich materials xLi(2)MnO(3)-(1-x)LiMO2 Molten-salt synthesis Nanocrystalline Li-ion batteries RECHARGEABLE LITHIUM BATTERIES SOLID-SOLUTION CATHODES ANOMALOUS CAPACITY MANGANESE-OXIDE OXYGEN LOSS ELECTRODES DIFFRACTION NANOWIRES STABILITY LIMN2O4 |
英文摘要 | Nanocrystalline Li[Li0.26Ni0.11Mn0.63]O2 were easily prepared by using Ni0.15Mn0.85(OH)(2) and Li2CO3 as precursors and KCI as melt-salt for the high capacity materials of Li-ion storage. The obtained nanopartides showed same morphology of polygonal shape and the particle size distribution increased with increasing sinter temperature. The Li[Li[0.26Ni0.11Mn0.63]O2 electrode sintered at 800 degrees C for 12 h exhibits a reversible capacity of more than 300 mAh g(-1) at 0.1 C rate between 2 V and 4.8V and the capacity retention remains 86% and 90% after 90 cycles at the rate of 0.5 C and 1 C, respectively. These superior electrochemical performances are discussed in detail and ascribed to the low dimension and well-crystallized particles. The low dimension provides a short diffusion path and fast transport channels for the lithium ion insertion/extraction reactions and the well-crystallized structure restrains the elimination of oxide ion vacancies and metal ions rearrangement during charge-discharge cycling. (C) 2013 Elsevier Ltd. All rights reserved.; http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=PARTNER_APP&SrcAuth=LinksAMR&KeyUT=WOS:000332812300039&DestLinkType=FullRecord&DestApp=ALL_WOS&UsrCustomerID=8e1609b174ce4e31116a60747a720701 ; Electrochemistry; SCI(E); 5; ARTICLE; dgxia@pku.edu.cn; 285-291; 117 |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/315841] |
专题 | 工学院 |
推荐引用方式 GB/T 7714 | Wang ZhenYao,Li Biao,Ma Jin,et al. The Enhanced Electrochemical Performance of Nanocrystalline Li[Li0.26Ni0.11Mn0.63]O-2 Synthesized by the Molten-Salt Method for Li-ion batteries[J]. 电化学学报,2014. |
APA | Wang ZhenYao,Li Biao,Ma Jin,&Xia DingGuo.(2014).The Enhanced Electrochemical Performance of Nanocrystalline Li[Li0.26Ni0.11Mn0.63]O-2 Synthesized by the Molten-Salt Method for Li-ion batteries.电化学学报. |
MLA | Wang ZhenYao,et al."The Enhanced Electrochemical Performance of Nanocrystalline Li[Li0.26Ni0.11Mn0.63]O-2 Synthesized by the Molten-Salt Method for Li-ion batteries".电化学学报 (2014). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论