Evolution of surface hardness of concrete under sulfate attack

doi:10.1016/j.conbuildmat.2013.11.107

CORC > 北京大学 > 工学院

	Evolution of surface hardness of concrete under sulfate attack
	Ouyang, Wei-yi ; Chen, Jian-kang ; Jiang, Min-qiang
刊名	construction and building materials
	2014
关键词	Surface hardness Sulfate attack Concrete Damage evolution CEMENT MORTAR SCHMIDT HAMMER ION DIFFUSION FLY-ASH EROSION ETTRINGITE RESISTANCE MECHANISM FRESH
DOI	10.1016/j.conbuildmat.2013.11.107
英文摘要	Under sulfate attack, the erosion damage is not uniformly distributed in concrete, but firstly takes place at the surface since the sulfate radical ions diffuse from surface to inner of the material. In order to investigate the damage degree, the variation of surface hardness of concrete was investigated in this study. The corrosion experiments continued about 330 days, and the evolution of surface hardness of concrete samples was detected by rebound method. Meanwhile, SEM observation and XRD test for concrete samples were also carried out. It was found that exist a competition mechanism of enhancement effect and weakening effect, because the surface hardness of concrete monotone increases at the initial stage. SEM observation and XRD test indicated that both enhancement and weakening effect are all caused by delayed ettringite and gypsum. The enhancement mechanism is produced by the filling effect of delayed ettringite and gypsum, and the weakening mechanism is induced by damage evolution due to their expansion force. Based on the experimental results, a new method was suggested to express the damage degree. The analysis results indicated that the water-to-cement ratio of concrete and the concentration of sulfate solution strongly affect the attenuation of the surface hardness. (C) 2013 Elsevier Ltd. All rights reserved.; Construction & Building Technology; Engineering, Civil; Materials Science, Multidisciplinary; SCI(E); EI; 0; ARTICLE; chenjiankang@nbu.edu.cn; 419-424; 53
语种	英语
内容类型	期刊论文
源URL	[http://ir.pku.edu.cn/handle/20.500.11897/215677]
专题	工学院
推荐引用方式 GB/T 7714	Ouyang, Wei-yi,Chen, Jian-kang,Jiang, Min-qiang. Evolution of surface hardness of concrete under sulfate attack[J]. construction and building materials,2014.
APA	Ouyang, Wei-yi,Chen, Jian-kang,&Jiang, Min-qiang.(2014).Evolution of surface hardness of concrete under sulfate attack.construction and building materials.
MLA	Ouyang, Wei-yi,et al."Evolution of surface hardness of concrete under sulfate attack".construction and building materials (2014).