HYDROGEN ABSORPTION PROPERTIES OF PSEUDO-BINARY ALLOYS TI0.8ZR0.2MN1.5M0.5 | |
HONG, CM ; ZHANG, YF ; HAN, DG | |
1994 | |
关键词 | HYDROGEN STORAGE TIMN2-BASE ALLOYS P-C-T MEASUREMENTS X-RAY DIFFRACTION HYDRIDES |
英文摘要 | Hydrogen absorption properties of Ti0.8Zr0.2Mn1.5M0.5 alloys have been investigated. The M represent the elements Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Al or Nb. All these alloys belong to Laves phase C14 (MgZn2) type structure and the lattice constants were measured. In order to aborb hydrogen it is necessary for the lattice constants a to be larger than 4.88 x 10(-10) m and c larger than 7.99 x 10(-10) m. V, Cr, Fe and Cu were appropriate elements to substitute for M. Especially, Ti0.8Zr0.2Mn1.5Cr0.5 alloy was an excellent candidate for hydrogen storage and purification. It exhibited perfect properties, i.e., a large capacity (H/M = 1.1), rapid hydrogen absorption, wide plateau [DELTA(H/W) = 0.95] and flat dissociation pressure of its hydride. With Al and Nb as the M the resultant alloys could also absorb a great quantity of hydrogen. But it was difficult to release the hydrogen and the plateau was destroyed. Ti0.8Zr0.2Mn1.5Ti0.5 Was not a single intermetallic compound though it absorbed hydrogen. With Mn, Co and Ni as M, the alloys did not absorb hydrogen.; Chemistry, Physical; SCI(E); 4 |
语种 | 英语 |
内容类型 | 其他 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/313442] |
专题 | 化学与分子工程学院 |
推荐引用方式 GB/T 7714 | HONG, CM,ZHANG, YF,HAN, DG. HYDROGEN ABSORPTION PROPERTIES OF PSEUDO-BINARY ALLOYS TI0.8ZR0.2MN1.5M0.5. 1994-01-01. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论