Investigation into diesel engine cylinder head failure | |
Jing, GX; Zhang, MX; Qu, S1; Pang, JC; Fu, CM; Dong, C; Li, SX; Xu, CG; Zhang, ZF | |
刊名 | ENGINEERING FAILURE ANALYSIS |
2018-08-01 | |
卷号 | 90页码:36-46 |
关键词 | Cylinder head Failure analysis Finite element method Thermal fatigue Crack morphology |
ISSN号 | 1350-6307 |
DOI | 10.1016/j.engfailanal.2018.03.008 |
英文摘要 | The failure analyses of the cast iron cylinder head of diesel engine, including the chemical composition, microstructure, mechanical properties, crack initiation and propagation, were studied in this paper. Based on the results, it was found that the most dangerous site analyzed by the dye penetrant inspection is the thinnest area of the bridge zone. In high temperature, the oxidation phenomenon becomes severe. The cracks initiate from the interface between the graphite and ferrite matrix in the surface of the cylinder head, and the oxide promotes the crack propagation. Failure of the engine cylinder head is mainly caused by the thermal fatigue, which was proved by the result of finite element method and crack morphology. Furthermore, the improvement of thermal conductivity of material is a useful way to enhance the service life of engine. |
学科主题 | Engineering, Mechanical ; Materials Science, Characterization & Testing |
语种 | 英语 |
WOS记录号 | WOS:000432858400004 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/80087] |
专题 | 金属研究所_中国科学院金属研究所 |
作者单位 | 1.China North Engine Res Inst, 96 Yongjin Rd, Tianjin 300400, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China |
推荐引用方式 GB/T 7714 | Jing, GX,Zhang, MX,Qu, S,et al. Investigation into diesel engine cylinder head failure[J]. ENGINEERING FAILURE ANALYSIS,2018,90:36-46. |
APA | Jing, GX.,Zhang, MX.,Qu, S.,Pang, JC.,Fu, CM.,...&Zhang, ZF.(2018).Investigation into diesel engine cylinder head failure.ENGINEERING FAILURE ANALYSIS,90,36-46. |
MLA | Jing, GX,et al."Investigation into diesel engine cylinder head failure".ENGINEERING FAILURE ANALYSIS 90(2018):36-46. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论