Controllable growth, structure, and low field emission of well-aligned CNx nanotubes | |
Wang, XB; Liu, LQ; Zhu, DB; Zhang, L; Ma, HZ; Yao, N; Zhang, BL | |
刊名 | JOURNAL OF PHYSICAL CHEMISTRY B |
2002-03-07 | |
卷号 | 106期号:9页码:2186-2190 |
ISSN号 | 1520-6106 |
DOI | 10.1021/jp013007r |
英文摘要 | A large area and controllable synthesis of well-aligned CKx nanotubes with a high content of nitrogen (x less than or equal to 9%) was carried out by pyrolyzing metal phthalocyanine on an n-type Si(100) substrate. The diameters of the CNx nanotubes range widely from 20 to 200 nm, and the lengths range from 1 to 100 mum. The impressive bamboo-like CNx nanotubes consist of a few uniform, small, and well-ordered compartments. Investigation on morphology and elemental composition of the CNx nanotubes suggests that the overall tube morphology depends strongly on the nitrogen concentration. The higher the N content, the more compartmentalized of nanotubes become, which results in the formation of more curved CNx nanotubes. Our studies show that three different types of N atoms can be present in these materials. These are "pyridinic", "pyrrolic", and "graphitic" nitrogen with binding energies of 398.1, 401.0, and 405.1 eV, respectively. Field emission measurements suggest that the CNx nanotubes began to emit electrons at an electric field of 1.5 V/mum, and current densities of 80,muA/cm(2) have been realized at an applied field as low as 2.6 V/mum. Doping carbon nanotubes with N enhances their electron-conducting properties because of the presence of additional lone pairs of electrons that act as donors with respect to the delocalized pi system of the hexagonal framework. The controllable synthesis of well-aligned CNx nanotubes with high N ratio may open a route to improve the field emission properties of nanotubes. |
语种 | 英语 |
出版者 | AMER CHEMICAL SOC |
WOS记录号 | WOS:000174403200011 |
内容类型 | 期刊论文 |
源URL | [http://ir.iccas.ac.cn/handle/121111/79439] |
专题 | 中国科学院化学研究所 |
通讯作者 | Zhang, BL |
作者单位 | 1.Chinese Acad Sci, Inst Chem, Ctr Mol Sci, Beijing 100080, Peoples R China 2.Zhengzhou Univ, Dept Phys, Zhengzhou 450052, Peoples R China 3.Chinese Acad Sci, Anhui Inst Opt & Fine Mech, Hefei 230031, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, XB,Liu, LQ,Zhu, DB,et al. Controllable growth, structure, and low field emission of well-aligned CNx nanotubes[J]. JOURNAL OF PHYSICAL CHEMISTRY B,2002,106(9):2186-2190. |
APA | Wang, XB.,Liu, LQ.,Zhu, DB.,Zhang, L.,Ma, HZ.,...&Zhang, BL.(2002).Controllable growth, structure, and low field emission of well-aligned CNx nanotubes.JOURNAL OF PHYSICAL CHEMISTRY B,106(9),2186-2190. |
MLA | Wang, XB,et al."Controllable growth, structure, and low field emission of well-aligned CNx nanotubes".JOURNAL OF PHYSICAL CHEMISTRY B 106.9(2002):2186-2190. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论