Polynaphthoxazine-montmorillonite nanocomposites: Synthesis and characterization | |
Wang, CY; Zhao, T; Han, B; Ke, YC | |
刊名 | ACTA POLYMERICA SINICA |
2002-04-01 | |
期号 | 2页码:217-220 |
关键词 | Naphthoxazines Montmorillonite Nanocomposites |
ISSN号 | 1000-3304 |
英文摘要 | A new class of phenolic-like thermosetting resins based on the ring-opening polymerization of naphthoxazine precursor exhibits some unique properties, including: no by-product releasing during curing reactions; near-zero shrinkage and excellent mechanical properties. Polynaphthoxazines-clay hybrid nanocomposites were prepared from I 5-dihydroxynaphthalene, aniline, formaldehyde and different proportion montmorillonite ( MMT) by in-situ reaction in ethanol. H-1-Nuclear Magnetic Resonance (H-1-NMR), X-ray Diffraction Analysis (XRD), Thermogravimetry (TGA) and Transmission Electron Microscopy (TEM) were applied to characterize the nanocomposites. H-1-NMR spectrum of naphthoxazine from the nanocomposites was identical to that of the pristine naphthoxazine, indicating the presence of MMT didn't change the chemical structure of the product. The spaces of silicate layers of montmorillonite in the composites were investigated by using X-ray diffractometer. It was found that exfoliation structure was formed after in-situ synthesis reaction and was remained after being cured. The TEM results suggested that an exfoliated poly-naphthoxazine-montmorillonite nanocomposite was successfully achieved. Dynamic TGA showed that only very small amount of clay is effective to improve the weight residues for nanocomposites. The char yield at 700degreesC increased by ca. 10% with 5 wt% MMT content in the nanocomposite and reached 65%. The confined crystallization behavior of the system was discussed. |
语种 | 英语 |
出版者 | SCIENCE CHINA PRESS |
WOS记录号 | WOS:000175207200017 |
内容类型 | 期刊论文 |
源URL | [http://ir.iccas.ac.cn/handle/121111/78775] |
专题 | 中国科学院化学研究所 |
通讯作者 | Wang, CY |
作者单位 | Chinese Acad Sci, Inst Chem, Ctr Mol Sci, Beijing 100080, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, CY,Zhao, T,Han, B,et al. Polynaphthoxazine-montmorillonite nanocomposites: Synthesis and characterization[J]. ACTA POLYMERICA SINICA,2002(2):217-220. |
APA | Wang, CY,Zhao, T,Han, B,&Ke, YC.(2002).Polynaphthoxazine-montmorillonite nanocomposites: Synthesis and characterization.ACTA POLYMERICA SINICA(2),217-220. |
MLA | Wang, CY,et al."Polynaphthoxazine-montmorillonite nanocomposites: Synthesis and characterization".ACTA POLYMERICA SINICA .2(2002):217-220. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论