Construction of mass-controllable mesoporous NiCo2S4 electrodes for high performance supercapacitors | |
Peng, Tao1; Qian, Zhongyu1; Wang, Jun1; Song, Dalei1; Liu, Jinyuan1; Liu, Qi1; Wang, Peng2 | |
刊名 | JOURNAL OF MATERIALS CHEMISTRY A |
2014 | |
卷号 | 2期号:45页码:19376-19382 |
ISSN号 | 2050-7488 |
DOI | 10.1039/c4ta04246h |
英文摘要 | 3D interconnected NiCo2S4 nanosheets have been directly grown on nickel foams using a facile two-step solution-based method. The as-prepared electrodes with controllable mass loadings and microstructures show excellent electrochemical performance, indicating their potential application as supercapacitors. Electrochemical measurements exhibit that the NiCo2S4/nickel foam electrode has a competitive areal specific capacitance (10.82 F cm(-2) at 10 mA cm(-2)), relatively high rate capability (40.3% capacitance retention at 80 mA cm(-2)) and good cycling stability (92% capacitance retention after 1500 cycles at 20 mA cm(-2)). |
语种 | 英语 |
出版者 | ROYAL SOC CHEMISTRY |
WOS记录号 | WOS:000344384000033 |
内容类型 | 期刊论文 |
源URL | [http://ir.iccas.ac.cn/handle/121111/52893] |
专题 | 中国科学院化学研究所 |
通讯作者 | Wang, Jun |
作者单位 | 1.Harbin Engn Univ, Key Lab Superlight Mat & Surface Technol, Minist Educ, Harbin 150001, Peoples R China 2.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Peoples R China |
推荐引用方式 GB/T 7714 | Peng, Tao,Qian, Zhongyu,Wang, Jun,et al. Construction of mass-controllable mesoporous NiCo2S4 electrodes for high performance supercapacitors[J]. JOURNAL OF MATERIALS CHEMISTRY A,2014,2(45):19376-19382. |
APA | Peng, Tao.,Qian, Zhongyu.,Wang, Jun.,Song, Dalei.,Liu, Jinyuan.,...&Wang, Peng.(2014).Construction of mass-controllable mesoporous NiCo2S4 electrodes for high performance supercapacitors.JOURNAL OF MATERIALS CHEMISTRY A,2(45),19376-19382. |
MLA | Peng, Tao,et al."Construction of mass-controllable mesoporous NiCo2S4 electrodes for high performance supercapacitors".JOURNAL OF MATERIALS CHEMISTRY A 2.45(2014):19376-19382. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论