Synthesis and responsive behavior of poly(N,N-dimethylaminoethyl methacrylate) brushes grafted on silica nanoparticles and their quaternized derivatives

doi:10.1016/j.polymer.2012.03.011

CORC > 化学研究所 > 中国科学院化学研究所

	Synthesis and responsive behavior of poly(N,N-dimethylaminoethyl methacrylate) brushes grafted on silica nanoparticles and their quaternized derivatives
	Dong, Zhixin; Wei, Hua; Mao, Jun; Wang, Dapeng; Yang, Muquan; Bo, Shuqin; Ji, Xiangling
刊名	POLYMER
	2012-04-25
卷号	53 期号:10 页码:2074-2084
关键词	Pdmaema Brushes Surface-initiated Atom Transfer Radical Polymerization Responsive Behavior
ISSN号	0032-3861
DOI	10.1016/j.polymer.2012.03.011
英文摘要	Poly(N,N-dimethylaminoethyl methacrylate) (PDMAEMA) was grafted onto the surface of silica nanoparticles via surface-initiated atom transfer radical polymerization to form temperature- and pH-responsive PDMAEMA brushes (silica-g-PDMAEMA). The resultant samples were characterized via H-1 NMR, transmission electron microscopy, atomic force microscopy, Fourier transform infrared spectroscopy, and thermogravimetric analysis. Their molecular weights and molecular weight distributions were determined by gel permeation chromatography analysis after silica content etching. The control of brush thickness and the responsive behavior were systematically investigated. Dynamic light scattering (DLS) results indicate that the brush thickness can be controlled by changing the polymerization time and the DMAEMA, initiator, and THF concentrations. According to DLS and zeta potential results, the lower critical solution temperature (LCST) of the PDMAEMA brushes shifts to a higher temperature with decreasing solution pH, which is attributed to the weak charge of the polyelectrolyte brushes. When the temperature is kept above the transition temperature, the silica-g-PDMAEMA nanoparticles aggregate into clusters and disaggregate during the cooling process. Moreover, with the heating/cooling step increasing, the aggregation and disaggregation temperatures are decreased. Meanwhile, when the molecular weight is increased from 13.6 x 10(4) to 23.1 x 10(4) g/mol, a decrease in the LCSTs at constant pH is observed. The related properties of the corresponding quaternized analog, poly([2-(methacryloyloxy) ethyl] trimethylammonium iodide) (PMETAI) brushes, were also discussed. The hydrodynamic radius of the silica-g-PMETAI nanoparticles decreases with increasing ionic strength, and a salting-out/salting-in effect is observed when the ionic strength is adjusted using NaI instead of NaCl. (C) 2012 Elsevier Ltd. All rights reserved.
语种	英语
出版者	ELSEVIER SCI LTD
WOS记录号	WOS:000304214500014
内容类型	期刊论文
源URL	[http://ir.iccas.ac.cn/handle/121111/47147]
专题	中国科学院化学研究所
通讯作者	Ji, Xiangling
作者单位	Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Grad Sch, Changchun 130022, Peoples R China
推荐引用方式 GB/T 7714	Dong, Zhixin,Wei, Hua,Mao, Jun,et al. Synthesis and responsive behavior of poly(N,N-dimethylaminoethyl methacrylate) brushes grafted on silica nanoparticles and their quaternized derivatives[J]. POLYMER,2012,53(10):2074-2084.
APA	Dong, Zhixin.,Wei, Hua.,Mao, Jun.,Wang, Dapeng.,Yang, Muquan.,...&Ji, Xiangling.(2012).Synthesis and responsive behavior of poly(N,N-dimethylaminoethyl methacrylate) brushes grafted on silica nanoparticles and their quaternized derivatives.POLYMER,53(10),2074-2084.
MLA	Dong, Zhixin,et al."Synthesis and responsive behavior of poly(N,N-dimethylaminoethyl methacrylate) brushes grafted on silica nanoparticles and their quaternized derivatives".POLYMER 53.10(2012):2074-2084.