	Preparation of PVDF-CTFE hydrophobic membrane by non-solvent induced phase inversion: Relation between polymorphism and phase inversion
	Zheng, Libing; Wang, Jun; Yu, Dawei; Zhang, Yong; Wei, Yuansong
刊名	JOURNAL OF MEMBRANE SCIENCE
	2018-03-15
卷号	550 页码:480-491
关键词	PVDF polymorphism Phase inversion LiCl Interconnectivity PVDF-CTFE
ISSN号	0376-7388
文献子类	Article
英文摘要	Semi-crystalline polymers poly(vinylidene fluoride) and PVDF-based copolymer were common membrane materials which have found broad application. In an attempt to illuminate the relation between phase inversion and the polymer crystalline polymorphism, the effect of LiCl on PVDF polymorphs, membrane morphology, pore structure, hydrophobicity, thermal property, and permeability were investigated for Poly(vinylidene fluoride-co-chlorotrifluoroethylene) (PVDF-CTFE) membrane prepared by non-solvent induced phase inversion method. Both thermodynamic and kinetic effect were observed, and LiCl was found to favor the crystallization process. The phase inversion route and rate were significantly influenced by LiCl, result in the increase of the content of beta-phase, membrane crystallinity, thermo-resistance, overall pore size, and pore interconnectivity when increase LiCl content. The surface pore size and porosity increased firstly when LiCl content was lower than 5%, but significantly decreased with more LiCl. Meanwhile, the pore interconnectivity was highly recommend for membrane evaluation as porosity was found delivering partial information. Membrane M5 presents optimal performance with a permeate flux of 21.85 kg/m(2) h and the permeate conductivity was lower than 15 mu S/cm at a temperature difference of 30 degrees C. This work demonstrates the relation between phase inversion and the crystalline structure and illuminate its effect on the final membrane. It provides a novel method for membrane mechanism research and membrane evaluation which can be instructive for PVDF membrane research and application.
内容类型	期刊论文
源URL	[http://ir.rcees.ac.cn/handle/311016/40830]
专题	生态环境研究中心_大气污染控制中心
推荐引用方式 GB/T 7714	Zheng, Libing,Wang, Jun,Yu, Dawei,et al. Preparation of PVDF-CTFE hydrophobic membrane by non-solvent induced phase inversion: Relation between polymorphism and phase inversion[J]. JOURNAL OF MEMBRANE SCIENCE,2018,550:480-491.
APA	Zheng, Libing,Wang, Jun,Yu, Dawei,Zhang, Yong,&Wei, Yuansong.(2018).Preparation of PVDF-CTFE hydrophobic membrane by non-solvent induced phase inversion: Relation between polymorphism and phase inversion.JOURNAL OF MEMBRANE SCIENCE,550,480-491.
MLA	Zheng, Libing,et al."Preparation of PVDF-CTFE hydrophobic membrane by non-solvent induced phase inversion: Relation between polymorphism and phase inversion".JOURNAL OF MEMBRANE SCIENCE 550(2018):480-491.