Effects of nano-sio2 modified emulsion sizing on the interfacial performance of carbon fiber reinforced plastics | |
Yang, Y; Lu, CX; Wang, XK; Liu, HP; He, F; Li, YH; Song, Y | |
刊名 | New carbon materials |
2005-09-01 | |
卷号 | 20期号:3页码:211-216 |
关键词 | Carbon fibers Nano-sio2 Sizing Dmta Ifss Ilss |
ISSN号 | 1007-8827 |
通讯作者 | Lu, cx(lucx@sxicc.ac.cn) |
英文摘要 | A single fiber fragmentation test, three-point bend test, scanning electron microscopy and dynamic mechanical thermal analysis (dmta) were performed to study the influence of nano-sio2 modified emulsion sizing on the interfacial properties of carbon fibers reinforced plastics (cfrp). as a comparison, cfrp with and without sizing but not modified by nano-sio2 were also investigated. results showed that the interfacial shear strength (ifss) values of the cf with modified sizing and unmodified sizing were increased by 79% and 41%, respectively, compared to the cf without sizing. the interlaminar shear strength (ilss) values of the cfrp with modified sizing and unmodified sizing were also increased by 14% and 9%, respectively compared to the cfrp without sizing. furthermore, the loss tangent (tan delta) of cfrp with modified sizing declined to 18% and glass transition temperature (t-g) was increased by 5 degrees c, compared to the cfrp with unmodified sizing in the dmta chart. so the interfacial adhesion performance of the cfrp with modified sizing by nano-sio2 was evidently increased. |
WOS关键词 | COMPOSITES ; INTERPHASE ; PITCH |
WOS研究方向 | Materials Science |
WOS类目 | Materials Science, Multidisciplinary |
语种 | 英语 |
出版者 | SCIENCE PRESS |
WOS记录号 | WOS:000232141100004 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2377830 |
专题 | 中国科学院大学 |
通讯作者 | Lu, CX |
作者单位 | 1.Chinese Acad Sci, Inst Coal Chem, Key Lab Carbon Mat, Taiyuan 030001, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China |
推荐引用方式 GB/T 7714 | Yang, Y,Lu, CX,Wang, XK,et al. Effects of nano-sio2 modified emulsion sizing on the interfacial performance of carbon fiber reinforced plastics[J]. New carbon materials,2005,20(3):211-216. |
APA | Yang, Y.,Lu, CX.,Wang, XK.,Liu, HP.,He, F.,...&Song, Y.(2005).Effects of nano-sio2 modified emulsion sizing on the interfacial performance of carbon fiber reinforced plastics.New carbon materials,20(3),211-216. |
MLA | Yang, Y,et al."Effects of nano-sio2 modified emulsion sizing on the interfacial performance of carbon fiber reinforced plastics".New carbon materials 20.3(2005):211-216. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论