Corrosion failure of marine steel in sea-mud containing sulfate reducing bacteria | |
Yanliang, H | |
刊名 | MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION
![]() |
2004-02-01 | |
卷号 | 55期号:2页码:124-127 |
ISSN号 | 0947-5117 |
DOI | 10.1002/maco.200303698 |
文献子类 | Article |
英文摘要 | The corrosion failure behavior of marine steel is affected by stress, which exists in offshore structures at sea-mud region. The sulfate reducing bacteria (SRB) in the sea-mud made the steel more sensitive to stress corrosion cracking (SCC) and weaken the corrosion fatigue endurance. In this paper, a kind of natural sea-mud containing SRB was collected. Both SCC tests by slow strain rate technique and corrosion fatigue tests were performed on a kind of selected steel in sea-mud with and without SRB at corrosion and cathodic potentials. After this, the electrochemical response of static and cyclic stress of the specimen with and without cracks in sea-mud was analyzed in order to explain the failure mechanism. Hydrogen permeation tests were also performed in the sea-mud at corrosion and cathodic potentials. It is concluded that the effect of SRB on environment sensitive fracture maybe explained as the consequences of the acceleration of SRB on corrosion rate and hydrogen entry into the metal.; The corrosion failure behavior of marine steel is affected by stress, which exists in offshore structures at sea-mud region. The sulfate reducing bacteria (SRB) in the sea-mud made the steel more sensitive to stress corrosion cracking (SCC) and weaken the corrosion fatigue endurance. In this paper, a kind of natural sea-mud containing SRB was collected. Both SCC tests by slow strain rate technique and corrosion fatigue tests were performed on a kind of selected steel in sea-mud with and without SRB at corrosion and cathodic potentials. After this, the electrochemical response of static and cyclic stress of the specimen with and without cracks in sea-mud was analyzed in order to explain the failure mechanism. Hydrogen permeation tests were also performed in the sea-mud at corrosion and cathodic potentials. It is concluded that the effect of SRB on environment sensitive fracture maybe explained as the consequences of the acceleration of SRB on corrosion rate and hydrogen entry into the metal. |
学科主题 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
URL标识 | 查看原文 |
语种 | 英语 |
WOS记录号 | WOS:000189160000007 |
公开日期 | 2010-12-21 |
内容类型 | 期刊论文 |
源URL | [http://ir.qdio.ac.cn/handle/337002/2321] ![]() |
专题 | 海洋研究所_海洋腐蚀与防护研究发展中心 |
作者单位 | Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China |
推荐引用方式 GB/T 7714 | Yanliang, H. Corrosion failure of marine steel in sea-mud containing sulfate reducing bacteria[J]. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,2004,55(2):124-127. |
APA | Yanliang, H.(2004).Corrosion failure of marine steel in sea-mud containing sulfate reducing bacteria.MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION,55(2),124-127. |
MLA | Yanliang, H."Corrosion failure of marine steel in sea-mud containing sulfate reducing bacteria".MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION 55.2(2004):124-127. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论