Synthesis of Mesoporous gamma-Alumina -Supported Co-Based Catalysts and Their Catalytic Performance for Chemoselective Reduction of Nitroarenes | |
Huang, Haigen[1]; Tang, Mingwu[2]; Wang, Xueguang[3]; Zhang, Man[4]; Guo, Shuoqiang[5]; Zou, Xiujing[6]; Lu, Xionggang[7] | |
刊名 | ACS APPLIED MATERIALS & INTERFACES |
2018 | |
卷号 | 10页码:5413-5428 |
关键词 | mesoporous alumina cobalt nitroarene aromatic amine reduction |
ISSN号 | 1944-8244 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2181547 |
专题 | 上海大学 |
作者单位 | 1.[1]Shanghai Univ, Sch Mat Sci & Engn, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China. 2.[2]Xiamen Univ, Dept Chem, Coll Chem & Chem Engn, Xiamen 361005, Peoples R China. 3.[3]Shanghai Univ, Sch Mat Sci & Engn, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China. 4.[4]Shanghai Univ, Sch Mat Sci & Engn, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China. 5.[5]Shanghai Univ, Sch Mat Sci & Engn, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China. 6.[6]Shanghai Univ, Sch Mat Sci & Engn, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China. 7.[7]Shanghai Univ, Sch Mat Sci & Engn, State Key Lab Adv Special Steel, Shanghai 200072, Peoples R China. |
推荐引用方式 GB/T 7714 | Huang, Haigen[1],Tang, Mingwu[2],Wang, Xueguang[3],et al. Synthesis of Mesoporous gamma-Alumina -Supported Co-Based Catalysts and Their Catalytic Performance for Chemoselective Reduction of Nitroarenes[J]. ACS APPLIED MATERIALS & INTERFACES,2018,10:5413-5428. |
APA | Huang, Haigen[1].,Tang, Mingwu[2].,Wang, Xueguang[3].,Zhang, Man[4].,Guo, Shuoqiang[5].,...&Lu, Xionggang[7].(2018).Synthesis of Mesoporous gamma-Alumina -Supported Co-Based Catalysts and Their Catalytic Performance for Chemoselective Reduction of Nitroarenes.ACS APPLIED MATERIALS & INTERFACES,10,5413-5428. |
MLA | Huang, Haigen[1],et al."Synthesis of Mesoporous gamma-Alumina -Supported Co-Based Catalysts and Their Catalytic Performance for Chemoselective Reduction of Nitroarenes".ACS APPLIED MATERIALS & INTERFACES 10(2018):5413-5428. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论