Effect of reverted austenite fraction on hydrogen embrittlement of TRIP-aided medium Mn steel (0.1C-5Mn) | |
Zhang, Yongjian[1]; Hui, Weijun[2]; Zhao, Xiaoli[3]; Wang, Cunyu[4]; Cao, Wenquan[5]; Dong, Han[6] | |
刊名 | ENGINEERING FAILURE ANALYSIS |
2019 | |
卷号 | 97页码:605-616 |
关键词 | Hydrogen embrittlement Medium Mn steel Reverted austenite Transformation-induced plasticity effect |
ISSN号 | 1350-6307 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2163676 |
专题 | 上海大学 |
作者单位 | 1.[1]Beijing Jiaotong Univ, Sch Mech Elect & Control Engn, Beijing 100044, Peoples R China. 2.[2]Beijing Jiaotong Univ, Sch Mech Elect & Control Engn, Beijing 100044, Peoples R China. 3.[3]Beijing Jiaotong Univ, Sch Mech Elect & Control Engn, Beijing 100044, Peoples R China. 4.[4]Cent Iron & Steel Res Inst, Beijing 100081, Peoples R China. 5.[5]Cent Iron & Steel Res Inst, Beijing 100081, Peoples R China. 6.[6]Shanghai Univ, Sch Mat Sci & Engn, Shanghai 200444, Peoples R China. |
推荐引用方式 GB/T 7714 | Zhang, Yongjian[1],Hui, Weijun[2],Zhao, Xiaoli[3],et al. Effect of reverted austenite fraction on hydrogen embrittlement of TRIP-aided medium Mn steel (0.1C-5Mn)[J]. ENGINEERING FAILURE ANALYSIS,2019,97:605-616. |
APA | Zhang, Yongjian[1],Hui, Weijun[2],Zhao, Xiaoli[3],Wang, Cunyu[4],Cao, Wenquan[5],&Dong, Han[6].(2019).Effect of reverted austenite fraction on hydrogen embrittlement of TRIP-aided medium Mn steel (0.1C-5Mn).ENGINEERING FAILURE ANALYSIS,97,605-616. |
MLA | Zhang, Yongjian[1],et al."Effect of reverted austenite fraction on hydrogen embrittlement of TRIP-aided medium Mn steel (0.1C-5Mn)".ENGINEERING FAILURE ANALYSIS 97(2019):605-616. |