Effect of the precipitated second phase during aging on the damping capacity degradation behavior of M2052 alloy | |
Zhang, Ying; Li, Ning; Yan, Jiazhen; Xie, Jinwu | |
刊名 | EIGHTH CHINA NATIONAL CONFERENCE ON FUNCTIONAL MATERIALS AND APPLICATIONS |
2014 | |
卷号 | Vol.873页码:36-41 |
关键词 | aging damping capacity degradation alpha-Mn interstitial solute atoms |
ISSN号 | 1022-6680 |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/1994632 |
专题 | 四川大学 |
作者单位 | Sichuan Univ, Sch Mfg Sci & Engn, Chengdu 610065, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, Ying,Li, Ning,Yan, Jiazhen,et al. Effect of the precipitated second phase during aging on the damping capacity degradation behavior of M2052 alloy[J]. EIGHTH CHINA NATIONAL CONFERENCE ON FUNCTIONAL MATERIALS AND APPLICATIONS,2014,Vol.873:36-41. |
APA | Zhang, Ying,Li, Ning,Yan, Jiazhen,&Xie, Jinwu.(2014).Effect of the precipitated second phase during aging on the damping capacity degradation behavior of M2052 alloy.EIGHTH CHINA NATIONAL CONFERENCE ON FUNCTIONAL MATERIALS AND APPLICATIONS,Vol.873,36-41. |
MLA | Zhang, Ying,et al."Effect of the precipitated second phase during aging on the damping capacity degradation behavior of M2052 alloy".EIGHTH CHINA NATIONAL CONFERENCE ON FUNCTIONAL MATERIALS AND APPLICATIONS Vol.873(2014):36-41. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论