Optical spectroscopy of Dy3+-doped CaGdAlO4single crystal for potential use in solid-state yellow lasers

doi:10.1016/j.optmat.2017.02.046

	Optical spectroscopy of Dy3+-doped CaGdAlO4single crystal for potential use in solid-state yellow lasers
	Xu, Xiaodong 1; Hu, Zongwen 1; Li, Ruijuan 2,3; Li, Dongzhen 1; Di, Juqing 4; Su, Liangbi 2; Yang, Qiuhong 3; Sai, Qinglin 5; Tang, Huili 6; Wang, Qingguo 6
刊名	Optical Materials
	2017
卷号	66 页码:469-473
ISSN号	09253467
DOI	10.1016/j.optmat.2017.02.046
英文摘要	The crystal growth, optical spectra and lifetime of Dy:CaGdAlO4crystal were investigated for the first time to our best knowledge. Single Dy:CaGdAlO4crystal with size of Φ4 × 40 mm3was grown by floating zone method. The peak absorption cross-sections were calculated to be 2.43 × 10−21cm2and 1.28 × 10−21 cm2 at 453 nm for σ and π polarizations. The Judd-Ofelt (JO) parameters of Ω2, Ω4and Ω6were calculated to be 1.8 × 10−20cm2, 1.0 × 10−20cm2and 0.5 × 10−20cm2, respectively. The emission cross-sections were calculated to be 0.51 × 10−20cm2and 0.55 × 10−20cm2for σ and π polarizations. The fluorescence decay time is 222 μs. The results indicate that the Dy:CaGdAlO4crystal is a potential candidate for yellow laser operation. © 2017 Elsevier B.V.
内容类型	期刊论文
源URL	[http://ir.sic.ac.cn/handle/331005/25596]
专题	中国科学院上海硅酸盐研究所
作者单位	1.Jiangsu Key Laboratory of Advanced Laser Materials and Devices, School of Physics and Electronic Engineering, Jiangsu Normal University, Xuzhou; 221116, China; 2.Key Laboratory of Transparent and Opto-functional Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Science, Shanghai; 201899, China; 3.School of Materials Science and Engineering, Shanghai University, Shanghai; 200444, China; 4.National Engineering & Technology Research Center of Scattered Metals, Vital Materials Co., Ltd., Qingyuan; 511517, China; 5.Key Laboratory of Materials for High Power Laser, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Science, Shanghai; 201800, China; 6.School of Physics Science and Engineering, Tongji University, Shanghai; 200092, China; 7.Institute of Low Temperature and Structure Research PAS, Okolna 2 Str, Wroclaw, Poland
推荐引用方式 GB/T 7714	Xu, Xiaodong,Hu, Zongwen,Li, Ruijuan,et al. Optical spectroscopy of Dy3+-doped CaGdAlO4single crystal for potential use in solid-state yellow lasers[J]. Optical Materials,2017,66:469-473.
APA	Xu, Xiaodong.,Hu, Zongwen.,Li, Ruijuan.,Li, Dongzhen.,Di, Juqing.,...&Xu, Jun.(2017).Optical spectroscopy of Dy3+-doped CaGdAlO4single crystal for potential use in solid-state yellow lasers.Optical Materials,66,469-473.
MLA	Xu, Xiaodong,et al."Optical spectroscopy of Dy3+-doped CaGdAlO4single crystal for potential use in solid-state yellow lasers".Optical Materials 66(2017):469-473.