Calcium Chloride Hexahydrate/Diatomite/Paraffin as Composite Shape-Stabilized Phase-Change Material for Thermal Energy Storage

CORC > 青海盐湖研究所 > 中国科学院青海盐湖研究所 > 青海盐湖研究所知识仓储

	Calcium Chloride Hexahydrate/Diatomite/Paraffin as Composite Shape-Stabilized Phase-Change Material for Thermal Energy Storage
	Zhang, Xinxing 1,2,3; Li, Xiang 1,3; Zhou, Yuan 1,3; Hai, Chunxi 1,3; Shen, Yue 1,3; Ren, Xiufeng 1,3; Zeng, Jinbo 1,3
刊名	ENERGY & FUELS
	2018
卷号	32 期号:1 页码:916-921
文献子类	Article
英文摘要	In this work, the calcium chloride hexahydrate/diatomite/paraffin composite phase-change material (PCM) was fabricated by impregnating calcium chloride hexahydrate into diatomite and further coating with paraffin. Scanning electron microscope (SEM) results showed that the hydrated salt could be impregnated into a diatomite well and the paraffin could be coated on a diatomite surface. The Fourier transform infrared spectroscopy (FT-IR) demonstrated that no chemical interactions were found between calcium chloride hexahydrate and diatomite matrix except that of hydrogen bonds. The melting and crystallizing enthalpy of the coated composite PCM are 108.2 and 98.5 J/g, respectively. The supercooling of hydrated salts was weakened due to the nucleation positions on the huge surface of diatomite and the coating effect of the paraffin, and phase segregation was eliminated in 100 cycles by microvolume effect in the pores of the diatoniite. Additionally, coated composite PCM and composite PCM exhibited better thermal stability and reliability than hydrated salts due to the interactions of hydrated bonds, the capillary force and the surface tension as well as the coating of the paraffin. After the 100 cycles, the melting and crystallizing enthalpy of coated composite PCM declined to 106.2 and 93.8 J/g from 108.2 and 98.5 J/g, dropping by 1.8% and 4.8%, respectively. The coated composite PCM with well thermal properties, thermal reliability, and chemical stability was a promising PCM candidate for heat-energy storage applications.
WOS关键词	HEAT-STORAGE ; GRAPHITE COMPOSITE ; CONDUCTIVITY ; DIATOMITE ; PCM ; HEXAHYDRATE ; PERFORMANCE ; HYDROLYSIS ; BUILDINGS ; CAPTURE
WOS研究方向	Energy & Fuels ; Engineering
语种	英语
WOS记录号	WOS:000423253200094
内容类型	期刊论文
源URL	[http://ir.isl.ac.cn/handle/363002/6379]
专题	青海盐湖研究所_青海盐湖研究所知识仓储青海盐湖研究所_盐湖资源与化学实验室
作者单位	1.Chinese Acad Sci, Qinghai Inst Salt Lakes, Key Lab Comprehens & Highly Efficient Utilizat Sa, Xining 810008, Qinghai, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China 3.Key Lab Salt Lake Resources Chem Qinghai Prov, Xining 810008, Qinghai, Peoples R China
推荐引用方式 GB/T 7714	Zhang, Xinxing,Li, Xiang,Zhou, Yuan,et al. Calcium Chloride Hexahydrate/Diatomite/Paraffin as Composite Shape-Stabilized Phase-Change Material for Thermal Energy Storage[J]. ENERGY & FUELS,2018,32(1):916-921.
APA	Zhang, Xinxing.,Li, Xiang.,Zhou, Yuan.,Hai, Chunxi.,Shen, Yue.,...&Zeng, Jinbo.(2018).Calcium Chloride Hexahydrate/Diatomite/Paraffin as Composite Shape-Stabilized Phase-Change Material for Thermal Energy Storage.ENERGY & FUELS,32(1),916-921.
MLA	Zhang, Xinxing,et al."Calcium Chloride Hexahydrate/Diatomite/Paraffin as Composite Shape-Stabilized Phase-Change Material for Thermal Energy Storage".ENERGY & FUELS 32.1(2018):916-921.