High Wear Resistance of Magnetron Sputtered Cr80Si20N Nanocomposite Coatings: Almost Independent of Hardness

CORC > 宁波材料技术与工程研究所 > 中国科学院宁波材料技术与工程研究所 > 2018专题

	High Wear Resistance of Magnetron Sputtered Cr80Si20N Nanocomposite Coatings: Almost Independent of Hardness
	Huang, Feng; Shao, Tao; Zhu, Ping; Li, Peng; Li, Ke; Jia, Congcong; Ge, Fangfang
刊名	TRIBOLOGY LETTERS
	2018
卷号	66 期号:2
关键词	Thin-films Behavior Mechanisms Toughness Corrosion Friction Ratio Oxide
英文摘要	Hardness has been popularly considered as an essential factor defining the wear resistance of hard coatings. Here, we report magnetron sputtered Cr80Si20N nanocomposite coatings, of widely varied packing densities, that exhibited identical specific wear rates, while the hardness changed over a wide range (from similar to 12 to similar to 36 GPa). All the Cr80Si20N coatings were free of extended and uninterrupted columnar boundaries, and retained low specific wear rates in the ball-on-plate sliding tests against Al2O3 counterpart with a normal load of 5 N (less than 3.0 x 10(-16) m(3)/N m under ambient condition and less than 2.0 x 10(-15) m(3)/N m under 3.5 wt% NaCl solution, respectively). Post examination reveals extensive interruption or termination of cracks in the wear tracks of the under-dense coatings, indicative of extrinsic toughening mechanisms by effective relief of local contact stress. Our results suggest that a critical role of toughening rather than hardening, played in enhancing the wear resistance of hard coatings, and thus would pave a way to develop highly wear-resistant coatings with a low hardness.
学科主题	Science & Technology - Other Topics ; Materials Science
语种	英语
公开日期	2018-12-04
内容类型	期刊论文
源URL	[http://ir.nimte.ac.cn/handle/174433/17457]
专题	2018专题
推荐引用方式 GB/T 7714	Huang, Feng,Shao, Tao,Zhu, Ping,et al. High Wear Resistance of Magnetron Sputtered Cr80Si20N Nanocomposite Coatings: Almost Independent of Hardness[J]. TRIBOLOGY LETTERS,2018,66(2).
APA	Huang, Feng.,Shao, Tao.,Zhu, Ping.,Li, Peng.,Li, Ke.,...&Ge, Fangfang.(2018).High Wear Resistance of Magnetron Sputtered Cr80Si20N Nanocomposite Coatings: Almost Independent of Hardness.TRIBOLOGY LETTERS,66(2).
MLA	Huang, Feng,et al."High Wear Resistance of Magnetron Sputtered Cr80Si20N Nanocomposite Coatings: Almost Independent of Hardness".TRIBOLOGY LETTERS 66.2(2018).