Metal Buffer Layer on Structure, Mechanical and Tribological Property of GLC films | |
Li Lei; Guo Peng; Liu Lin-Lin; Sun Li-Li; Wang Ai-Ying; Ke Pei-Ling | |
刊名 | JOURNAL OF INORGANIC MATERIALS |
2018 | |
卷号 | 33期号:3页码:331-338 |
关键词 | Carbon-films Coatings Environments Performance Deposition Adhesion Water Friction Behavior Ti6al4v |
英文摘要 | Graphite-like carbon films (GLC) with different metal buffer layers (Cr, Ti, W) were fabricated by direct current magnetron sputtering technique. The effect of metal buffer layer on structure and tribological properties in artificial seawater were carefully investigated. The results show that, in contrast to Ti/GLC and W/GLC film, Cr/GLC film has the highest sp(2) hybridization content, which increases from the top layer to Cr/C interface. The highest sp2 hybridization content promotes graphitization degree of the tribo-film which acts as lubrication phase in the sliding process. The results of potentiodynamic polarization tests show that, in all of three GLC films, Cr/GLC film shows superior corrosion resistance with the highest corrosion voltage (E-corr) of -0.16 V and the lowest corrosion current (i(corr)) of 4.42x10(-9) A/cm(2). As a result, Cr/GLC film presents the best tribological properties in artificial seawater in contrast to Ti/GLC and W/GLC films. |
学科主题 | Materials Science |
语种 | 英语 |
公开日期 | 2018-12-04 |
内容类型 | 期刊论文 |
源URL | [http://ir.nimte.ac.cn/handle/174433/16752] |
专题 | 2018专题 |
推荐引用方式 GB/T 7714 | Li Lei,Guo Peng,Liu Lin-Lin,et al. Metal Buffer Layer on Structure, Mechanical and Tribological Property of GLC films[J]. JOURNAL OF INORGANIC MATERIALS,2018,33(3):331-338. |
APA | Li Lei,Guo Peng,Liu Lin-Lin,Sun Li-Li,Wang Ai-Ying,&Ke Pei-Ling.(2018).Metal Buffer Layer on Structure, Mechanical and Tribological Property of GLC films.JOURNAL OF INORGANIC MATERIALS,33(3),331-338. |
MLA | Li Lei,et al."Metal Buffer Layer on Structure, Mechanical and Tribological Property of GLC films".JOURNAL OF INORGANIC MATERIALS 33.3(2018):331-338. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论