One step preparation of pure tau-MnAl phase with high magnetization using strip casting method | |
Wang, Changsheng; Shao, Zhuyin; Zhao, Hui; Zeng, Jiling; Zhang, Yinfeng; Yang, Wenyun; Lai, Youfang; Guo, Shuai; Du, Honglin; Yang, Yingchang | |
刊名 | AIP ADVANCES |
2017 | |
卷号 | 7期号:5页码:56213 |
ISSN号 | 2158-3226 |
英文摘要 | Ferromagnetic phase of Mn-Al exhibits great potential in the rare-earth free permanent magnetic materials due to its high magnetocrystalline anisotropy, high magnetization, high Curie temperature and low cost. In this work, the strip casting technique was applied to prepare MnAl magnetic phase. X-ray diffraction and energy dispersive X-ray analyses indicate that the as-prepared Mn54Al46 strip sample consists of pure tau-MnAl magnetic phase. It is found that the composition of Mn54Al46 is suitable to prepare tau-MnAl phase during the strip casting process. The Mn54Al46 strip sample synthesized through the strip casting exhibits a fairly high magnetization of 114 emu/g under a field of 5 T, while the coercivity of iHc = 2.8 kOe, magnetization of M-5T = 63.9 emu/g at room temperature can be obtained for Mn54Al46 powder sample. This preparation method can produce a large amount of tau-phase MnAl alloy and promote mass industrialized production. (C) 2017 Author(s). |
公开日期 | 2017-12-25 |
内容类型 | 期刊论文 |
源URL | [http://ir.nimte.ac.cn/handle/174433/13855] |
专题 | 2017专题 |
推荐引用方式 GB/T 7714 | Wang, Changsheng,Shao, Zhuyin,Zhao, Hui,et al. One step preparation of pure tau-MnAl phase with high magnetization using strip casting method[J]. AIP ADVANCES,2017,7(5):56213. |
APA | Wang, Changsheng.,Shao, Zhuyin.,Zhao, Hui.,Zeng, Jiling.,Zhang, Yinfeng.,...&Yang, Jinbo.(2017).One step preparation of pure tau-MnAl phase with high magnetization using strip casting method.AIP ADVANCES,7(5),56213. |
MLA | Wang, Changsheng,et al."One step preparation of pure tau-MnAl phase with high magnetization using strip casting method".AIP ADVANCES 7.5(2017):56213. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论