High temperature effects on irradiation damage of Ti2AlC

CORC > 宁波材料技术与工程研究所 > 中国科学院宁波材料技术与工程研究所 > 2017专题

	High temperature effects on irradiation damage of Ti2AlC
	Liu, Shaoshuai; Wang, Chenxu; Yang, Tengfei; Fang, Yuan; Huang, Qing; Wang, Yugang
刊名	NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS
	2017
卷号	406 页码:662-669
ISSN号	0168-583X
英文摘要	As one of the MAX phases, Ti2AlC combines attractive properties of both ceramics and metals, and has been suggested for potential nuclear reactor applications due to its excellent resistance to irradiation. This work is aimed at investigating the high temperature effects on evolution of irradiation damage in the MAX phase Ti2AlC. Ti2AlC was irradiated with 1.1 MeV C4+ ions at 298 K and 873 K with fluences ranging from 2 x 10(15) cm(-2) to 6 x 1016 cm(-2). Scanning electron microscopy (SEM), Raman spectra, grazing incidence X-ray diffraction (GIXRD), transmission electron microscopy (TEM), and nanoindentation were used to characterize the evolution of microstructures and mechanical properties at both temperatures. Significant crackings along grain boundaries were observed in 298 K, which were not observed in the samples irradiated at 837 K. No amorphization was found in the GIXRD analyses and TEM characterization, and some fcc phases were formed during high dose irradiation at 298 K. Raman spectra show that all the vibration modes of Ti2AlC decreased severely in room temperature irradiation, but they nearly remained unchanged in high temperature irradiation at the dose of 2 x 10(15) cm(-2). Nanoindentation shows significant hardening for Ti2AlC irradiated at high temperature, suggesting the presence of irradiation -induced defects. The current study reveals that the irradiation tolerance of Ti2AlC is significantly improved with increasing temperature, demonstrating the great potential of Ti2AlC for using in advanced nuclear reactors. (C) 2017 Elsevier B.V. All rights reserved.
公开日期	2017-12-25
内容类型	期刊论文
源URL	[http://ir.nimte.ac.cn/handle/174433/13646]
专题	2017专题
推荐引用方式 GB/T 7714	Liu, Shaoshuai,Wang, Chenxu,Yang, Tengfei,et al. High temperature effects on irradiation damage of Ti2AlC[J]. NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS,2017,406:662-669.
APA	Liu, Shaoshuai,Wang, Chenxu,Yang, Tengfei,Fang, Yuan,Huang, Qing,&Wang, Yugang.(2017).High temperature effects on irradiation damage of Ti2AlC.NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS,406,662-669.
MLA	Liu, Shaoshuai,et al."High temperature effects on irradiation damage of Ti2AlC".NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS 406(2017):662-669.