The effect of ball-milling time and annealing temperature on fracture toughness of Ni-3 wt.% SiC using small punch testing

doi:10.1016/j.matchar.2018.02.024

CORC > 上海应用物理研究所 > 中国科学院上海应用物理研究所 > 中科院上海应用物理研究所2011-2017年

	The effect of ball-milling time and annealing temperature on fracture toughness of Ni-3 wt.% SiC using small punch testing
	Yang, C ; Wei, T ; Muransky, O ; Carr, D ; Huang, HF ; Zhou, XT
刊名	MATERIALS CHARACTERIZATION
	2018
卷号	138 页码:289-295
关键词	Metal-matrix Composites Ion irradiatIon Alloy Nanoparticles Embrittlement Dispersion Reactor Steels Damage
ISSN号	1044-5803
DOI	10.1016/j.matchar.2018.02.024
文献子类	期刊论文
英文摘要	A set of dispersion strengthened Ni-3 wt.% SiC samples have been prepared via a powder metallurgy route for an application in molten salt reactor (MSR) systems. A mixture of 97 wt.% Ni and 3 wt.% SiC powder was prepared by varying the ball-milling time (8, 24, 36 and 48 h). The ball-milling process was followed by powder consolidation using spark plasma sintering (SPS) and rapid cooling to room temperature. The samples were then annealed at different temperatures (300 degrees C, 700 degrees C and 850 degrees C). The fracture behaviour of the Ni-3 wt.% SiC samples was investigated using the Small Punch Test (SPT). A scanning electron microscope (SEM) with energy dispersive spectrometer (EDS) and electron back-scatter diffraction (EBSD), as well as transmission electron microscopy (TEM) were employed to examine the microstructure of the tested Ni-3 wt.% SiC samples. The obtained results show that the SPT fracture energy is strongly dependent on the grain size of Ni matrix, which is affected by ball-milling times and annealing temperature. It has been further found that the segregation of large SiC particles at grain boundaries promotes intergranular fracture and thus significantly reduces the fracture energy. The results indicate that the distribution and size of SiC particles at grain boundary is mainly affected by the ball-milling time. Hence, the ball-milling time governs the fracture toughness of Ni-3 wt.% SiC samples.
语种	英语
WOS记录号	WOS:000428483400032
内容类型	期刊论文
源URL	[http://ir.sinap.ac.cn/handle/331007/29174]
专题	上海应用物理研究所_中科院上海应用物理研究所2011-2017年
作者单位	1.Yang, C 2.Wei, T 3.Muransky, O 4.Carr, D 5.Huang, HF 6.Zhou, XT
推荐引用方式 GB/T 7714	Yang, C,Wei, T,Muransky, O,et al. The effect of ball-milling time and annealing temperature on fracture toughness of Ni-3 wt.% SiC using small punch testing[J]. MATERIALS CHARACTERIZATION,2018,138:289-295.
APA	Yang, C,Wei, T,Muransky, O,Carr, D,Huang, HF,&Zhou, XT.(2018).The effect of ball-milling time and annealing temperature on fracture toughness of Ni-3 wt.% SiC using small punch testing.MATERIALS CHARACTERIZATION,138,289-295.
MLA	Yang, C,et al."The effect of ball-milling time and annealing temperature on fracture toughness of Ni-3 wt.% SiC using small punch testing".MATERIALS CHARACTERIZATION 138(2018):289-295.