Superhydrophilic Antireflective Periodic Mesoporous Organosilica Coating on Flexible Polyimide Substrate with Strong Abrasion Resistance | |
Wang, J; Zhang, C; Yang, CM; Zhang, C; Wang, MC; Zhang, J; Xu, Y | |
刊名 | ACS APPLIED MATERIALS & INTERFACES |
2017 | |
卷号 | 9期号:6页码:5468-5476 |
关键词 | Antireflective Pmo Coating Superhydrophilic Polyimide Abrasion-resistance |
ISSN号 | 1944-8244 |
DOI | 10.1021/acsami.6b14117 |
文献子类 | 期刊论文 |
英文摘要 | Superhydrophilic antireflective periodic mesoporous organosilica (PMO) coating was prepared on flexible polyimide substrate via solvent evaporation-induced self-assembly (SEISM method, in which tetraethoxysilane (TEOS) and a special bridged silsesquioxane were used as reactants. The bridged silsesquioxane, EG-BSQ was synthesized through the stoichiometric reaction between 3-glycidoxyporpyltrimethoxysilane (GPTMS) and ethylene diamine (EDA). Under the influence of surfactant, TEOS and EG-BSQ co-condensed and enclosed the ordered mesporous in the coating. The results of grazing-incidence small-angle X-ray scattering (GISAXS) and the transmission electron microscope (TEM) indicated that the mesopores belonged to a Fmmm orthorhombic symmetry structure. With increasing EG-BSQ concentration, the mesoporous structure in the PMO coating becomes more and more disordered because silica mesopore walls shrunk or collapsed during calcination and consequently the refractive index of PMO coating became larger. The antireflective (AR) PMO coating showed an optical transmittance of 99.54% on polyimide (PI) much higher than the 88.68% of bare PI. The water contact angle of PMO coating was less than 9.0, which indicated the AR PMO coating was superhydrophilic. Moreover, the PMO coating showed an excellent mechanical property, the transmittance of the PMO coating displayed a very low loss of 0.1% after abrasion of 25 cycles by CS-10F wearaser. |
语种 | 英语 |
WOS记录号 | WOS:000394481800048 |
内容类型 | 期刊论文 |
源URL | [http://ir.sinap.ac.cn/handle/331007/27459] |
专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
推荐引用方式 GB/T 7714 | Wang, J,Zhang, C,Yang, CM,et al. Superhydrophilic Antireflective Periodic Mesoporous Organosilica Coating on Flexible Polyimide Substrate with Strong Abrasion Resistance[J]. ACS APPLIED MATERIALS & INTERFACES,2017,9(6):5468-5476. |
APA | Wang, J.,Zhang, C.,Yang, CM.,Zhang, C.,Wang, MC.,...&Xu, Y.(2017).Superhydrophilic Antireflective Periodic Mesoporous Organosilica Coating on Flexible Polyimide Substrate with Strong Abrasion Resistance.ACS APPLIED MATERIALS & INTERFACES,9(6),5468-5476. |
MLA | Wang, J,et al."Superhydrophilic Antireflective Periodic Mesoporous Organosilica Coating on Flexible Polyimide Substrate with Strong Abrasion Resistance".ACS APPLIED MATERIALS & INTERFACES 9.6(2017):5468-5476. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论