Fabrication of methylammonium bismuth iodide through interdiffusion of solution-processed BiI3/CH3NH3I stacking layers

	Fabrication of methylammonium bismuth iodide through interdiffusion of solution-processed BiI3/CH3NH3I stacking layers
	Wang, Huijia 1,2; Tian, Jianhua 1; Jiang, Kejian 2; Zhang, Yu 1,2; Fan, Haochen 2; Huang, Jinhua 2; Yang, Lian-ming 2; Guan, Bo 2; Song, Yanlin 2
刊名	RSC ADVANCES
	2017
卷号	7 期号:69 页码:43826-43830
英文摘要	Methylammonium bismuth iodide (MA(3)Bi(2)I(9)) perovskite, has been deposited on a mesoporous TiO2 film with high homogeneousity and coverage through interdiffusion of solution-processed BiI3/CH3NH3I stacking layers, resulting in higher power conversion efficiency in the perovskite solar cell as compared with that prepared using a conventional one-step solution method.
语种	英语
内容类型	期刊论文
源URL	[http://ir.iccas.ac.cn/handle/121111/41051]
专题	化学研究所_绿色印刷实验室
作者单位	1.Tianjin Univ, Sch Chem Engn & Technol, Tianjin 300072, Peoples R China 2.Chinese Acad Sci, Inst Chem, Key Lab Green Printing, Beijing 100190, Peoples R China
推荐引用方式 GB/T 7714	Wang, Huijia,Tian, Jianhua,Jiang, Kejian,et al. Fabrication of methylammonium bismuth iodide through interdiffusion of solution-processed BiI3/CH3NH3I stacking layers[J]. RSC ADVANCES,2017,7(69):43826-43830.
APA	Wang, Huijia.,Tian, Jianhua.,Jiang, Kejian.,Zhang, Yu.,Fan, Haochen.,...&Song, Yanlin.(2017).Fabrication of methylammonium bismuth iodide through interdiffusion of solution-processed BiI3/CH3NH3I stacking layers.RSC ADVANCES,7(69),43826-43830.
MLA	Wang, Huijia,et al."Fabrication of methylammonium bismuth iodide through interdiffusion of solution-processed BiI3/CH3NH3I stacking layers".RSC ADVANCES 7.69(2017):43826-43830.