Sintering process investigation during polytetrafluoroethylene hollow fibre membrane fabrication by extrusion method | |
Zhou, Meiqing1; Cao, Yiming1; Jia, Jingxuan1,2; Kang, Guodong1; Zou, Tong1,2; Li, Meng1 | |
刊名 | HIGH PERFORMANCE POLYMERS |
2017-11-01 | |
卷号 | 29期号:9页码:1069-1082 |
关键词 | PTFE extrusion fabrication hollow fibre membrane sintering membrane properties |
英文摘要 | In this study, the effect of sintering conditions including manner, temperature and duration on properties of polytetrafluoroethylene (PTFE) hollow fibre membrane fabricated by extrusion method was intensively investigated. Different from un-sintered and relaxed sintered, the fixed sintered PTFE hollow fibre membrane was observed to generate a uniform fibril-node' porous structure and a main crystal transformation to folded chain crystal with smaller size. Consequently, it was found that for fixed setting sintering, both temperature increase from 340 degrees C to 400 degrees C and duration prolongation obviously improved pore size, ethanol permeation performance and mechanical strength. Additionally, the test results revealed that the membrane sintered below virgin melting point (350 degrees C) had a noticeable higher porosity but poorer ethanol permeation performance that could be primarily attributed to increased ratio of closed pore. The sintering condition exhibited evident influence on PTFE hollow fibre membrane thermal stability, though it showed no alteration to the thermal decomposition of PTFE. The obtained PTFE hollow fibre membrane was tested to evaluate their vacuum membrane distillation (VMD) performances. It was found that PTFE membrane from lower sintering temperature delivered a better salt rejection; on the other hand, the permeate flux was improved by increased vacuum pressure during VMD operation. |
WOS标题词 | Science & Technology ; Physical Sciences |
类目[WOS] | Polymer Science |
研究领域[WOS] | Polymer Science |
关键词[WOS] | PTFE POROUS MEMBRANE ; MOLECULAR-WEIGHT ; CRYSTALLINE-STRUCTURE ; POLY(TETRAFLUOROETHYLENE) ; MELT ; POWDER ; PASTE ; DISTILLATION ; TEMPERATURE ; MECHANISM |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000414466300008 |
内容类型 | 期刊论文 |
源URL | [http://cas-ir.dicp.ac.cn/handle/321008/149754] |
专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
作者单位 | 1.Chinese Acad Sci, Dalian Inst Chem Phys, Dalian Natl Lab Clean Energy, Dalian 116023, Peoples R China 2.Univ Chinese Acad Sci, Beijing, Peoples R China |
推荐引用方式 GB/T 7714 | Zhou, Meiqing,Cao, Yiming,Jia, Jingxuan,et al. Sintering process investigation during polytetrafluoroethylene hollow fibre membrane fabrication by extrusion method[J]. HIGH PERFORMANCE POLYMERS,2017,29(9):1069-1082. |
APA | Zhou, Meiqing,Cao, Yiming,Jia, Jingxuan,Kang, Guodong,Zou, Tong,&Li, Meng.(2017).Sintering process investigation during polytetrafluoroethylene hollow fibre membrane fabrication by extrusion method.HIGH PERFORMANCE POLYMERS,29(9),1069-1082. |
MLA | Zhou, Meiqing,et al."Sintering process investigation during polytetrafluoroethylene hollow fibre membrane fabrication by extrusion method".HIGH PERFORMANCE POLYMERS 29.9(2017):1069-1082. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论