High transparency Cr,Nd:LuAG ceramics prepared with MgO additive

CORC > 上海光学精密机械研究所 > 中国科学院上海光学精密机械研究所 > 中科院强激光材料重点实验室

	High transparency Cr,Nd:LuAG ceramics prepared with MgO additive
	Zhang, Pande; Chai, Baoyan; Jiang, Benxue; Jiang, Yiguang; Chen, Shuilin; Gan, Qijun; Fan, Jintai; Mao, Xiaojian; Zhang, Long
刊名	J. Eur. Ceram. Soc.
	2017
卷号	37 期号:6 页码:2459
通讯作者	jiangsic@foxmail.com ; lzhang@siom.ac.cn
英文摘要	Cr (0.2 at.%) and Nd (0.8 at.%) co-doped Lu3Al5O12 ceramics were fabricated with MgO as the sintering additive. The addition of a small amount of MgO can affect the grain boundary mobility and influence the number and location of micropores in ceramics during the sintering process. The results show that when the MgO content is 0.02 wt.%, high-transparency Cr,Nd:LuAG ceramics can be obtained by vacuum sintering at 1670 degrees C for 5 h followed by hot isostatic pressing (HIP) post-sintering at 1750 degrees C in an argon atmosphere (P = 200 MPa) for 5 h. The optimum in-line transmittance of the HIPed Cr,Nd:LuAG ceramics (3 mm thick) is 83.5% at a wavelength of 840 nm and 84.0% at 710 nm. (C) 2017 Published by Elsevier Ltd.
收录类别	SCI
资助信息	National Natural Science Foundation of China [61378069, 61405221, 61308021]; Youth Innovation Promotion Association of the CAS
WOS记录号	WOS:000397359300017
内容类型	期刊论文
源URL	[http://ir.siom.ac.cn/handle/181231/28095]
专题	上海光学精密机械研究所_中科院强激光材料重点实验室
作者单位	中国科学院上海光学精密机械研究所
推荐引用方式 GB/T 7714	Zhang, Pande,Chai, Baoyan,Jiang, Benxue,et al. High transparency Cr,Nd:LuAG ceramics prepared with MgO additive[J]. J. Eur. Ceram. Soc.,2017,37(6):2459.
APA	Zhang, Pande.,Chai, Baoyan.,Jiang, Benxue.,Jiang, Yiguang.,Chen, Shuilin.,...&Zhang, Long.(2017).High transparency Cr,Nd:LuAG ceramics prepared with MgO additive.J. Eur. Ceram. Soc.,37(6),2459.
MLA	Zhang, Pande,et al."High transparency Cr,Nd:LuAG ceramics prepared with MgO additive".J. Eur. Ceram. Soc. 37.6(2017):2459.