Crystallization of weakly segregated poly(styrene-b-epsilon-caprolactone) diblock copolymer in thin films | |
Zhang FJ ; Huang HY ; Hu ZJ ; Chen YZ ; He TB | |
刊名 | langmuir |
2003 | |
卷号 | 19期号:24页码:10100-10108 |
关键词 | ATOMIC-FORCE MICROSCOPY ABC TRIBLOCK COPOLYMERS BLOCK-COPOLYMERS POLYMER CRYSTALLIZATION CONFINED CRYSTALLIZATION MICROPHASE SEPARATION POLY(ETHYLENE OXIDE) CRYSTAL ORIENTATIONS SELF-ORGANIZATION POLYSTYRENE BLOCK |
ISSN号 | 0743-7463 |
通讯作者 | zhang fj |
中文摘要 | the surface morphology and crystallization behavior of a weakly segregated symmetric diblock copolymer, poly(styrene-b-6-caprolactone) (ps-b-pcl), in thin films were investigated by optical microscopy, x-ray photoelectron spectroscopy, and atomic force microscopy (afm). when the samples were annealed in the molten state, surface-induced ordering, that is, relief structures with uniform thickness or droplets in the adsorbed monolayer, were observed depending on the annealing temperature. the polar pcl block preferred to wet the surface of a silicon wafer, while the ps block wet the air interface. this asymmetric wetting behavior led to the adsorbed monolayer with a pcl block layer having a thickness of around 4.0 nm. the crystallization of pcl blocks could overwhelm the microphase-separated structure because of the weak segregation. in situ observation of crystal growth indicated that the nucleation process preferred to occur at the edge of the thick parts of the film, that is, the relief structures or droplets. the crystal growth rate was presented by the time dependence of the distance between the tip of crystal clusters and the edge. at 22 and 17 degreesc, the average crystal growth rates were 55 +/- 10 and 18 +/- 4 nm/min, respectively. |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000186694500019 |
公开日期 | 2010-09-13 |
内容类型 | 期刊论文 |
源URL | [http://202.98.16.49/handle/322003/17193] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Zhang FJ,Huang HY,Hu ZJ,et al. Crystallization of weakly segregated poly(styrene-b-epsilon-caprolactone) diblock copolymer in thin films[J]. langmuir,2003,19(24):10100-10108. |
APA | Zhang FJ,Huang HY,Hu ZJ,Chen YZ,&He TB.(2003).Crystallization of weakly segregated poly(styrene-b-epsilon-caprolactone) diblock copolymer in thin films.langmuir,19(24),10100-10108. |
MLA | Zhang FJ,et al."Crystallization of weakly segregated poly(styrene-b-epsilon-caprolactone) diblock copolymer in thin films".langmuir 19.24(2003):10100-10108. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论