| 题名 | 微波介质陶瓷Ba5Nb4O15的低温烧结和MCT凝胶注模成型的工艺研究; Low-temperature Sintering of Ba5Nb4O15-based Microwave Dielectric Ceramics and Gel-casting of MCT ceramics |
| 作者 | 张冲 |
| 答辩日期 | 2007 ; 2007 |
| 导师 | 熊兆贤 |
| 关键词 | 微波介质陶瓷 Ba5Nb4O15 低温烧结 介电性能 凝胶注模成型 Microwave dielectric ceramics Ba5Nb4O15 Low-temperature sintering Dielectric properties Gel-casting |
| 英文摘要 | 本论文采用传统的固相法低温制备Ba5Nb4O15陶瓷，研究了烧结助剂、B位离子取代和工艺因素对陶瓷结构与介电性能的影响，并对陶瓷介电机理进行初步的探讨，还应用凝胶注模成型工艺制作了MCT陶瓷微波器件。 分别采用B2O3、LiF和B2O3-Bi2O3添加对Ba5Nb4O15陶瓷进行低温烧结，并对低温烧结行为、显微结构以及微波介电性能进行研究。实验发现少量B2O3、LiF添加可有效降低Ba5Nb4O15陶瓷的烧结温度至920℃左右；而B2O3-Bi2O3联合添加则随Bi2O3加入量的增加烧结温度先略有降低后升高；三种助剂均可在一定程度上改善Ba5Nb4O15陶瓷的谐振频率温度系数(τf)，同时也...; In this thesis, Ba5Nb4O15 ceramics were prepared via conventional mixing oxide route, and the effects of sintering aid, ionic substitutions and processing factors on chemical structure and dielectric properties of the samples were systematically investigated. Dielectric mechanisms of the ceramic were also discussed in this thesis. In addition, gel-casting forming process was used to fabricate micr...; 学位：工学硕士; 院系专业：化学化工学院材料科学与工程系_材料学; 学号：200436023 |
| 语种 | zh_CN |
| 出处 | http://210.34.4.13:8080/lunwen/detail.asp?serial=16246 |
| 内容类型 | 学位论文 |
| 源URL | [http://dspace.xmu.edu.cn/handle/2288/21642]  |
| 专题 | 材料学院－学位论文 |
| 推荐引用方式 GB/T 7714 | 张冲. 微波介质陶瓷Ba5Nb4O15的低温烧结和MCT凝胶注模成型的工艺研究, Low-temperature Sintering of Ba5Nb4O15-based Microwave Dielectric Ceramics and Gel-casting of MCT ceramics[D]. 2007, 2007. |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论