Underpotential deposition-induced synthesis of composition-tunable Pt-Cu nanocrystals and their catalytic properties | |
Jiang, Yaqi ; Jia, Yanyan ; Zhang, Jiawei ; Zhang, Lei ; Huang, Huang ; Xie, Zhaoxiong ; Zheng, Lansun ; Jiang YQ(蒋亚琪) ; Xie ZX(谢兆雄) ; Zheng LS(郑兰荪) | |
刊名 | http://dx.doi.org/10.1002/chem.201203729
![]() |
2013-02-25 | |
关键词 | Alloys Ammonium compounds Catalyst activity Cerium alloys Chlorine compounds Copper Copper alloys Dimethylformamide Electrocatalysis Formic acid Nanocrystals Nanoparticles Platinum |
英文摘要 | Pt-Cu alloy octahedral nanocrystals (NCs) have been synthesized successfully by using N,N-dimethylformamide as both the solvent and the reducing agent in the presence of cetyltrimethylammonium chloride. Cu underpotential deposition (UPD) is found to play a key role in the formation of the Pt-Cu alloy NCs. The composition in the Pt-Cu alloy can be tuned by adjusting the ratio of metal precursors in solution. However, the Cu content in the Pt-Cu alloy NCs cannot exceed 50 %. Due to the fact that Cu precursor cannot be reduced to metallic copper and the Cu content cannot exceed 50 %, we achieved the formation of the Pt-Cu alloy by using Cu UPD on the Pt surface. In addition, the catalytic activities of Pt-Cu alloy NCs with different composition were investigated in electrocatalytic oxidation of formic acid. The results reveal that the catalytic performance is strongly dependent on Pt-Cu alloy composition. The sample of Pt50Cu50 exhibits excellent activity in electrocatalytic oxidation of formic acid. A composed performance: Pt-Cu alloys have been prepared by directly incorporating underpotential-deposited Cu into the Pt lattice. The catalytic performances of the corresponding Pt-Cu alloy nanocrystals are strongly enhanced in comparison with commercial Pt/C catalysts (see figure). Copyright ? 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim. |
语种 | 英语 |
出版者 | Wiley-VCH Verlag |
内容类型 | 期刊论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/89124] ![]() |
专题 | 化学化工-已发表论文 |
推荐引用方式 GB/T 7714 | Jiang, Yaqi,Jia, Yanyan,Zhang, Jiawei,et al. Underpotential deposition-induced synthesis of composition-tunable Pt-Cu nanocrystals and their catalytic properties[J]. http://dx.doi.org/10.1002/chem.201203729,2013. |
APA | Jiang, Yaqi.,Jia, Yanyan.,Zhang, Jiawei.,Zhang, Lei.,Huang, Huang.,...&郑兰荪.(2013).Underpotential deposition-induced synthesis of composition-tunable Pt-Cu nanocrystals and their catalytic properties.http://dx.doi.org/10.1002/chem.201203729. |
MLA | Jiang, Yaqi,et al."Underpotential deposition-induced synthesis of composition-tunable Pt-Cu nanocrystals and their catalytic properties".http://dx.doi.org/10.1002/chem.201203729 (2013). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论