光Fenton反应的Ce-Fe/Al2O3催化剂超声制备及性能表征

CORC > 集美大学

	光Fenton反应的Ce-Fe/Al2O3催化剂超声制备及性能表征
	张亚平 ; 韦朝海 ; 吴超飞
刊名	http://epub.edu.cnki.net/grid2008/brief/detailj.aspx?filename=zyxz200711029&dbcode=CJFQ&dbname=CJFQ2007
	2012-06-05 ; 2012-06-05
关键词	水处理高级氧化光Fenton反应非均相催化剂超声 water treatment advanced oxidation photo-Fenton reaction heterogeneous catalyst ultrasonic X703
其他题名	Ultrasonic preparation and characterization of CeO2 doped with Fe/Al2O3 catalyst in photo-Fenton reaction
中文摘要	采用超声浸渍法和普通浸渍法制备具有相同铁负载量的Ce-Fe/Al2O3催化剂,以解决光Fenton反应过程中催化剂活性低的问题。通过扫描电镜(SEM)、氢程序升温还原(H2-TPR)、紫外可见漫反射(DRS)、比表面积分析(BET)及XPS等手段分别表征催化剂的表面形貌、还原性能、光吸收特性、比表面积特性及活性组分铁的价态和表面分布,利用媒介黄的光Fenton脱色反应考察催化剂的活性和稳定性。结果表明:超声浸渍20 min使活性组分Fe2O3分散均匀,有效抑制Fe2O3颗粒的长大,增加催化剂对光的吸收;比表面积从221.3增大到247.8 m2/g,改善了催化剂的微孔结构;催化剂表面铁含量从0.24%提高到0.38%,提高了催化剂的催化活性。在pH6.0条件下,60 min内可使200 mg/L媒介黄完全脱色。; Ce-Fe/Al2O3 catalysts possessing the same iron load amount were prepared with and without ultrsonic assitant during the impregnation step to solve the problem of low activity of catalyst in the process of photo-Fenton reaction.The surface morphology,reduction property,optical absorption characteristic,BET surface area and valency of Fe and surface distribution of catalysts were characterized through SEM,H2-TPR,DRS,BET and XPS analysis respectively.Activity and stability of catalysts were estimated by utilizing photo-Fenton decoloration reaction of medium yellow(MY10).The results show that catalyst prepared by ultrasonic treatment for 20 min causes activated component Fe2O3 to be highly dispersed.The growth of Fe2O3 particles is inhibited and the optical absorption increases.BET surface area increases from 221.3 to 247.8 m2/g and micropore structure is improved.The Fe content in catalyst surface increases from 0.24% to 0.38% and the catalytic activity of catalyst is improved.This catalyst can cause discoloring of MY10 under the condition of pH 6.0 in 60 min.; 【作者单位】华南理工大学环境科学与工程学院；华南理工大学环境科学与工程学院广州510640；集美大学环境工程研究所；厦门361021；广州510640；【作者英文名】ZHANG Ya-ping1,2,WEI Chao-hai1,WU Chao-fei1(1.School of Environmental Science and Engineering,South China University of Technology,Guangzhou 510640,China;2.Institute of Environmental Engineering,Jimei University,Xiamen 361021,China)
语种	中文
内容类型	期刊论文
源URL	[http://ir.calis.edu.cn/hdl/235041/18278]
专题	集美大学
推荐引用方式 GB/T 7714	张亚平,韦朝海,吴超飞. 光Fenton反应的Ce-Fe/Al2O3催化剂超声制备及性能表征[J]. http://epub.edu.cnki.net/grid2008/brief/detailj.aspx?filename=zyxz200711029&dbcode=CJFQ&dbname=CJFQ2007,2012, 2012.
APA	张亚平,韦朝海,&吴超飞.(2012).光Fenton反应的Ce-Fe/Al2O3催化剂超声制备及性能表征.http://epub.edu.cnki.net/grid2008/brief/detailj.aspx?filename=zyxz200711029&dbcode=CJFQ&dbname=CJFQ2007.
MLA	张亚平,et al."光Fenton反应的Ce-Fe/Al2O3催化剂超声制备及性能表征".http://epub.edu.cnki.net/grid2008/brief/detailj.aspx?filename=zyxz200711029&dbcode=CJFQ&dbname=CJFQ2007 (2012).