水泥-矿渣复合胶凝材料的水化C-S-H凝胶的长龄期特征 | |
王喆 ; 王强 ; 王栋民 ; WANG Zhe ; WANG Qiang ; WANG Dong-min | |
2016-03-30 ; 2016-03-30 | |
关键词 | 水泥 矿渣 C-S-H凝胶 长龄期特性 sea sand concrete corrosion resistance offshore construction TQ177 |
其他题名 | Long-term characteristics of the C-S-H produced by the hydration of cement-GGBS composite binder |
中文摘要 | 研究了掺50%矿渣的水泥-矿渣复合胶凝材料3 a龄期的硬化浆体C-S-H凝胶特性,结果显示:3 a龄期时矿渣反应程度为68.3%,大部分小颗粒矿渣已反应,但许多大颗粒矿渣几乎未反应;长龄期时浆体中Ca(OH)2没有消耗殆尽,从SEM图像中可以发现Ca(OH)2大量存在;水泥-矿渣复合胶凝材料体系3 a龄期的C-S-H凝胶的Ca/Si比、(Al+Mg)/Si比均值分别为1.88和0.60,相较于水泥生成的C-S-H凝胶,水泥-矿渣复合胶凝体系的C-S-H凝胶Ca/Si比较低,且含有大量Al。但Ca/Si比明显高于水泥-粉煤灰复合胶凝材料生成的C-S-H凝胶。; The 3-year characteristics of the C-S-H gel produced by hydration of cement-GGBS composite binder containing 50% slag were investigated. The results show that the reaction degree of slag is 68. 3% at the age of 3 years. Most of the small GGBS particles react heavily but many large particles remain almost unreacted. The Ca( OH)2in long-term hardened paste is not consumed completely,and a lot of Ca( OH)2can be observed in the SEM photograph. The mean Ca / Si,and( Al + Mg) / Si atom ratios of the gel in the 3-year hardened cement-GGBS paste are 1. 88 and 0. 60,respectively. The gel produced by cement-GGBS binder has a lower Ca / Si atom ratio and higher Al content than that of Portland cement paste. But the Ca / Si of the gel produced by cement-GGBS binder is much higher than that of the gel produced by cement-fly ash binder. |
语种 | 中文 ; 中文 |
内容类型 | 期刊论文 |
源URL | [http://ir.lib.tsinghua.edu.cn/ir/item.do?handle=123456789/149136] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | 王喆,王强,王栋民,等. 水泥-矿渣复合胶凝材料的水化C-S-H凝胶的长龄期特征[J],2016, 2016. |
APA | 王喆,王强,王栋民,WANG Zhe,WANG Qiang,&WANG Dong-min.(2016).水泥-矿渣复合胶凝材料的水化C-S-H凝胶的长龄期特征.. |
MLA | 王喆,et al."水泥-矿渣复合胶凝材料的水化C-S-H凝胶的长龄期特征".(2016). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论