Mechanical Properties of Steels Treated by Q-P-T Process Incorporating Carbide-free-bainite/martensite Multiphase Microstructure | |
Zhun-li TAN ; Kai-kai WANG ; Gu-hui GAO ; Xiao-lu GUI ; Bing-zhe BAI ; Yu-qing WENG ; Zhun-li TAN ; Kai-kai WANG ; Gu-hui GAO ; Xiao-lu GUI ; Bing-zhe BAI ; Yu-qing WENG | |
2016-03-30 ; 2016-03-30 | |
关键词 | carbide-free bainite multiphase microstructure quenching-partitioning-tempering partitioning time mechanical property TG142.15 |
其他题名 | Mechanical Properties of Steels Treated by Q-P-T Process Incorporating Carbide-free-bainite / martensite Multiphase Microstructure |
中文摘要 | Quenching-partitioning-tempering(Q-P-T)process were applied to a quenched carbide-free bainite/martensite(CFB/M)multiphase steel 40Mn2Si2Cr and its effect on the mechanical properties was studied.The results showed that the partitioning time of Q-P-T treatment can be increased greatly to 90min or even longer.The tensile strength,elongation and product of strength and elongation(PSE)of the experimental steel can achieve 1 650MPa,about 20%and over 33GPa�,respectively.The significant increase of partitioning time and excellent mechanical properties could be related to the CFB microstructure introduced in the quenching process during the Q-P-T treatment.; Quenching-partitioning-tempering(Q-P-T)process were applied to a quenched carbide-free bainite/martensite(CFB/M)multiphase steel 40Mn2Si2Cr and its effect on the mechanical properties was studied.The results showed that the partitioning time of Q-P-T treatment can be increased greatly to 90min or even longer.The tensile strength,elongation and product of strength and elongation(PSE)of the experimental steel can achieve 1 650MPa,about 20%and over 33GPa�,respectively.The significant increase of partitioning time and excellent mechanical properties could be related to the CFB microstructure introduced in the quenching process during the Q-P-T treatment. |
语种 | 英语 ; 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.lib.tsinghua.edu.cn/ir/item.do?handle=123456789/141794] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Zhun-li TAN,Kai-kai WANG,Gu-hui GAO,et al. Mechanical Properties of Steels Treated by Q-P-T Process Incorporating Carbide-free-bainite/martensite Multiphase Microstructure[J],2016, 2016. |
APA | Zhun-li TAN.,Kai-kai WANG.,Gu-hui GAO.,Xiao-lu GUI.,Bing-zhe BAI.,...&Yu-qing WENG.(2016).Mechanical Properties of Steels Treated by Q-P-T Process Incorporating Carbide-free-bainite/martensite Multiphase Microstructure.. |
MLA | Zhun-li TAN,et al."Mechanical Properties of Steels Treated by Q-P-T Process Incorporating Carbide-free-bainite/martensite Multiphase Microstructure".(2016). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论