Preparation and mechanical properties of ZrB2-based laminated composites | |
Wang Hailong ; Wang Chang'an ; Zhang Rui ; Hu Xing ; Huang Yong | |
2010-05-10 ; 2010-05-10 | |
关键词 | zirconium diboride laminated composites ultrahigh temperature ceramics reinforcement Materials Science, Multidisciplinary Metallurgy & Metallurgical Engineering |
中文摘要 | ZrB2/MO laminated composites, in which ZrB2 containing 10 vol% nano-SiC whiskers and 10 vol% SiC particles were taken as matrix layer and Mo as interfacial layer were prepared by roll-compaction and hot-pressing sintering at 1950 degrees C for 1 h under 20 MPa pressure in flow argon. The results show that the ZrB2/MO laminated composites have a high fracture toughness of 9.3 +/- 0.21 MPa-m(1/2), and the bending strength can be increased to 400 36 MPa by the addition of Si and B into the Mo layers, which would avoid cracking from layer interface and improve the brittlement of Mo at room temperature. The main mechanisms of enhancing toughness are attributed to crack bluntness, crack deflection, and crack parallel propagation along interfacial layers. MoB, ZrB and Mo5SiB2 were formed as the reaction among ZrB2, SiC and Mo, which would limit the increase of the strength and toughness. |
语种 | 中文 ; 中文 |
出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH ; SHAANXI ; C/O RARE METAL MATERIAL ENGINEERING PRESS, PO BOX 51, XIAN, SHAANXI 710016, PEOPLES R CHINA |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/21508] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Wang Hailong,Wang Chang'an,Zhang Rui,et al. Preparation and mechanical properties of ZrB2-based laminated composites[J],2010, 2010. |
APA | Wang Hailong,Wang Chang'an,Zhang Rui,Hu Xing,&Huang Yong.(2010).Preparation and mechanical properties of ZrB2-based laminated composites.. |
MLA | Wang Hailong,et al."Preparation and mechanical properties of ZrB2-based laminated composites".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论