	Stress corrosion cracking in the heat affected zone of a stainless steel 308L-316L weld joint in primary water
	Dong, Lijin ; Peng, Qunjia ; Han, En-Hou ; Ke, Wei ; Wang, Lei
刊名	CORROSION SCIENCE
	2016-06-01
卷号	107 页码:172-181
关键词	Stainless steel SEM TEM Stress corrosion Welding
ISSN号	0010-938X
通讯作者	Peng, QJ (reprint author), Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China.
学科主题	Materials Science ; Metallurgy & Metallurgical Engineering
收录类别	SCI
资助信息	Hundred-Talent program of Chinese Academy of Sciences; National Natural Science Foundation of China [51571204]
语种	英语
公开日期	2016-08-22
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/75863]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	Dong, Lijin,Peng, Qunjia,Han, En-Hou,et al. Stress corrosion cracking in the heat affected zone of a stainless steel 308L-316L weld joint in primary water[J]. CORROSION SCIENCE,2016,107:172-181.
APA	Dong, Lijin,Peng, Qunjia,Han, En-Hou,Ke, Wei,&Wang, Lei.(2016).Stress corrosion cracking in the heat affected zone of a stainless steel 308L-316L weld joint in primary water.CORROSION SCIENCE,107,172-181.
MLA	Dong, Lijin,et al."Stress corrosion cracking in the heat affected zone of a stainless steel 308L-316L weld joint in primary water".CORROSION SCIENCE 107(2016):172-181.