Printable poly(methylsilsesquioxane) dielectric ink and its application in solution processed metal oxide thin-film transistors | |
Wu, XZ(吴馨洲); Chen, Z(陈征); Zhou, T(周腾); Shao, SS(邵霜霜); Xie, ML(谢美兰); Song, MS(宋民顺); Cui, Z(崔铮) | |
刊名 | RSC ADVANCES |
2015 | |
卷号 | 5期号:27页码:7 |
通讯作者 | Chen, Z (陈征) |
英文摘要 | Thermally cross-linkable poly(methylsilsesquioxane) (PMSQ) has been investigated as a printable dielectric ink to make the gate insulator for solution processed metal oxide (IGZO) thin-film transistors by aerosol jet printing. It was found that by increasing the curing temperature from 150 to 200 degrees C, the dielectric constant and loss tangent of the printed PMSQ layer reduces dramatically. The mobility, leakage current and gate current of the PMSQ enabled thin-film transistor reduces accordingly, while the on/off ratio increases with the increase of curing temperature. An interfacial layer was introduced to further improve the on/off ratio to 3 x 10(5) and reduce the leakage current to 2.6 x 10(-10) A, which is the best result for the solution processed IGZO thin-film transistors using the PMSQ as the gate insulator at a curing temperature of only 150 degrees C. The study has demonstrated the feasibility of fabricating IGZO thin-film transistors by an all solution-based process. |
收录类别 | SCI |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.sinano.ac.cn/handle/332007/3491] |
专题 | 苏州纳米技术与纳米仿生研究所_印刷电子学部_崔铮团队 |
推荐引用方式 GB/T 7714 | Wu, XZ,Chen, Z,Zhou, T,et al. Printable poly(methylsilsesquioxane) dielectric ink and its application in solution processed metal oxide thin-film transistors[J]. RSC ADVANCES,2015,5(27):7. |
APA | Wu, XZ.,Chen, Z.,Zhou, T.,Shao, SS.,Xie, ML.,...&Cui, Z.(2015).Printable poly(methylsilsesquioxane) dielectric ink and its application in solution processed metal oxide thin-film transistors.RSC ADVANCES,5(27),7. |
MLA | Wu, XZ,et al."Printable poly(methylsilsesquioxane) dielectric ink and its application in solution processed metal oxide thin-film transistors".RSC ADVANCES 5.27(2015):7. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论